- 密度 [g/cm3]: 0.9525
- 拉伸强度 [MPa]: 24.1
- 弯曲模量 [MPa]: 0.965
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9525 g/cc | 0.03441 lb/in³ | ASTM D792 | ||
| Environmental Stress Crack Resistance | 48 hour | 48 hour | Fo; Compression molded parts prepared according to ASTM D 1928, condition B.; ASTM D1693 | ||
| High Load Melt Index | 21 g/10 min @Load 21.6 kg, Temperature 190 °C | 21 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | ||
| Melt Index of Compound | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 62 | 62 | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D2240 | ||
| Tensile Strength at Break | 31.7 MPa | 4600 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 | ||
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 | ||
| Elongation at Break | 800 % | 800 % | Compression molded parts prepared according to ASTM D 1928 Procedure C.; ASTM D638 | ||
| Flexural Modulus | 0.965 GPa | 140 ksi | Compression molded parts prepared according to ASTM D 1928, method 1, procedure B.; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | Compression molded parts prepared according to ASTM D 1928, procedure A.; ASTM D746 | ||
| Descriptive Properties | |||||
| Notched Constant Ligament Stress hours, min | 24 | ASTM F2136 | |||