- 密度 [g/cm3]: 0.949
- 拉伸强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.855
- 热变形温度 [℃]: 66.1
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | >= 1500 hour @Temperature 50.0 °C | >= 1500 hour @Temperature 122 °F | F50; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| High Load Melt Index | 10 g/10 min @Load 21.6 kg, Temperature 190 °C | 10 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 | 57 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 36.5 MPa | 5300 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 22.8 MPa | 3300 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 900 % | 900 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.855 GPa | 124 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 462 kJ/m² | 220 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 54.4 °C | 130 °F | Dow Method (DSC) |
| Crystallization Temperature | 117 °C | 243 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 66.1 °C | 151 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |