- 熔体流动速率 [g/10min]: 90.0
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 21.0
- 弯曲强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 0.910
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | |
| Melt Flow | 90 g/10 min @Load 2.16 kg | 90 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | |
| Tensile Strength, Yield | 21.0 MPa | 3050 psi | |
| Elongation at Break | 150 % | 150 % | |
| Modulus of Elasticity | 0.621 GPa | 90.1 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.910 GPa | 132 ksi | |
| Izod Impact Resistance | 1.10 J/cm² | 5.24 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 123 °C | 253 °F | |