- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 0.954
- 拉伸强度 [MPa]: 20.7
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 1.01
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | |
| Viscosity | 90000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 90000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 220000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 220000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 360000 cP @Shear Rate 300 1/s, Temperature 190 °C | 360000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg | 7.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 17.0 MPa | 2470 psi | |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | |
| Elongation at Break | 700 % | 700 % | |
| Modulus of Elasticity | 0.669 GPa | 97.0 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 1.01 GPa | 146 ksi | |
| Izod Impact Resistance | 12.3 J/cm² | 58.5 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 124 °C | 255 °F | |