- 熔体流动速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.949
- 吸水率 [%]: 0.01
- 缺口冲击强度: 0.8
- 拉伸强度 [MPa]: 24.0
- 弯曲模量 [MPa]: 1.14
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D792 |
| Water Absorption | 0.010 % | 0.010 % | ASTM D570 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50; ASTM D1693 |
| Oxidative Induction Time (OIT) | 10 min | 10 min | ASTM D3895 |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| Elongation at Break | 650 % | 650 % | ASTM D638 |
| Flexural Modulus | 1.14 GPa | 165 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | Notched/Unnotched not specified; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 130 °C | 266 °F | ASTM D3417 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D696 |