- 熔体流动速率 [g/10min]: 18.0
- 密度 [g/cm3]: 0.956
- 拉伸强度 [MPa]: 29.0
- 弯曲模量 [MPa]: 1.15
- 热变形温度 [℃]: 75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.956 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 190 °C | 18 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | ASTM D638 |
| Elongation at Yield | 7.7 % | 7.7 % | ASTM D638 |
| Flexural Modulus | 1.15 GPa | 167 ksi | 2% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | Unannealed (0.250 in); ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |