- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.965
- 热变形温度 [℃]: 76.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.965 g/cc | 0.0349 lb/in³ | ASTM D1505 |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 |
| Spiral Flow | 40.6 cm | 16.0 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength at Break | 31.6 MPa | 4580 psi | ASTM D638 |
| 1% Secant Modulus | 1500 MPa | 217000 psi | Crosshead speed - 0.5" min; ASTM D790 |
| 2% Secant Modulus | 1.23 GPa | 179 ksi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |