- 熔体流动速率 [g/10min]: 0.057
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Melt Flow | 0.057 g/10 min | 0.057 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 26.2 MPa | 3800 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 23.4 MPa | 3400 psi | ASTM D882 |
| Film Elongation at Break, MD | 300 % | 300 % | ASTM D882 |
| Film Elongation at Break, TD | 420 % | 420 % | ASTM D882 |
| Elmendorf Tear Strength MD | 14 g | 14 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 35 g | 35 g | ASTM D1922 |
| Dart drop Total Energy | 1090 J/cm | 2.05 ft-lb/mil | ASTM D3420 |
| Film Tensile Strength at Break, MD | 58.6 MPa | 8500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.5 MPa | 5000 psi | ASTM D882 |
| 1% Secant Modulus, MD | 793 MPa | 115000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 965 MPa | 140000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 216 °C | 390 - 421 °F | |