- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 25.5 MPa | 3700 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 26.2 MPa | 3800 psi | ASTM D882 |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 750 % | 750 % | ASTM D882 |
| Elmendorf Tear Strength MD | 18 g | 18 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 900 g | 900 g | ASTM D1922 |
| 1% Secant Modulus, MD | 862 MPa | 125000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 1000 MPa | 145000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | Typical Extrusion |