- 熔体流动速率 [g/10min]: 0.07
- 密度 [g/cm3]: 0.952
- 拉伸强度 [MPa]: 26.0
- 弯曲强度 [MPa]: 35.0
- 弯曲模量 [MPa]: 1.18
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | 1000 hour @Temperature 50.0 °C | 1000 hour @Temperature 122 °F | ASTM D1693 B |
| Melt Flow | 0.070 g/10 min @Load 2.16 kg | 0.070 g/10 min @Load 4.76 lb | ASTM D1238 |
| High Load Melt Index | 9.0 g/10 min @Load 21.6 kg | 9.0 g/10 min @Load 47.6 lb | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | >= 750 % | >= 750 % | ASTM D638 |
| Flexural Modulus | 1.18 GPa | 171 ksi | ASTM D790 |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | Equate Test Method |
| Crystallization Temperature | 116 °C | 241 °F | Equate Test Method |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 204 °C | 399 °F | |
| Zone 2 | 204 °C | 399 °F | |
| Zone 3 | 204 °C | 399 °F | |
| Zone 4 | 204 °C | 399 °F | |
| Die Temperature | 204 °C | 399 °F | |
| Melt Temperature | 210 °C | 410 °F | |
| Head Temperature | 204 °C | 399 °F | |