- 熔体流动速率 [g/10min]: 2.4
- 密度 [g/cm3]: 0.964
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.964 g/cc | 0.0348 lb/in³ | ExxonMobil Method | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 2.4 g/10 min | 2.4 g/10 min | 190°C/2.16 kg; ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 31.72 MPa | 4600 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 27.58 MPa | 4000 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 790 % | 790 % | ASTM D882 | ||
| Film Elongation at Break, TD | 6.0 % | 6.0 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 9.0 g | 9.0 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 | ||
| Dart drop Test | 50.0 g | 0.110 lb | ASTM D1790 | ||
| Film Tensile Strength at Break, MD | 43.44 MPa | 6300 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 38.61 MPa | 5600 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 1034.21 MPa | 150000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 1516.85 MPa | 220000 psi | ASTM D882 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||