- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.958
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | Exxon Method |
| Thickness | 12.7 microns | 0.500 mil | |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | Exxon Method (I2). HLMI (I21) is 20 g/10 min. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 400 % | 400 % | ASTM D882 |
| Secant Modulus, MD | 1.24 GPa | 180 ksi | ASTM D882 |
| Secant Modulus, TD | 1.275 GPa | 184.9 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.315 g/micron | 8.00 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 9.06 g/micron | 230 g/mil | ASTM D1922 |
| Dart Drop | 1.57 g/micron | 40.0 g/mil | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 71.0 MPa | 10300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 56.0 MPa | 8120 psi | ASTM D882 |