- 熔体流动速率 [g/10min]: 0.07
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Thickness | 15.2 microns | 0.600 mil | |
| Melt Flow | 0.070 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.070 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| High Load Melt Index | 12 g/10 min @Load 21.6 kg, Temperature 190 °C | 12 g/10 min @Load 47.6 lb, Temperature 374 °F | Condition F; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 445 % | 445 % | ASTM D882 |
| Film Elongation at Break, TD | 547 % | 547 % | ASTM D882 |
| Elmendorf Tear Strength MD | 8.0 g | 8.0 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 79 g | 79 g | ASTM D1922 |
| Dart drop Test | 373 g | 0.822 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 58.43 MPa | 8475 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.70 MPa | 7208 psi | ASTM D882 |
| 1% Secant Modulus, MD | 517 MPa | 75000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 917 MPa | 133000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131 °C | 268 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 4.0 | 4.0 | |