- 熔体流动速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.937
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.937 g/cc | 0.0339 lb/in³ | ISO 1183 |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 2.1 g/10 min @Load 5.00 kg, Temperature 190 °C | 2.1 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 530 % | 530 % | ISO 527-3 |
| Film Elongation at Break, TD | 830 % | 830 % | ISO 527-3 |
| Tensile Modulus | 0.450 GPa | 65.3 ksi | MD; ASTM D882-A |
| 0.540 GPa | 78.3 ksi | TD; ASTM D882-A | |
| Coefficient of Friction | 0.40 | 0.40 | ISO 8295 |
| Elmendorf Tear Strength, MD | 3.80 g/micron | 96.5 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 25.5 g/micron | 648 g/mil | ISO 6383/2 |
| Dart drop Test | 130 g @Thickness 0.0400 mm | 0.287 lb @Thickness 0.00157 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 56.0 MPa | 8120 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 39.0 MPa | 5660 psi | ISO 527-3 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 190 - 210 °C | 374 - 410 °F | |