- 熔体流动速率 [g/10min]: 5.1
- 密度 [g/cm3]: 0.935
- 吸水率 [%]: 0.01
- 拉伸强度 [MPa]: 18.0
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | Base Resin; ASTM D792 | ||
| 0.946 g/cc | 0.0342 lb/in³ | Compounded; ASTM D792 | |||
| Water Absorption | 0.010 % | 0.010 % | ASTM D570 | ||
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50; Condition B, 100% Igepal; ASTM D1693 | ||
| Oxidative Induction Time (OIT) | 10 min | 10 min | Condition 220°C, in oxygen environment; ASTM D3895 | ||
| Melt Flow | 5.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 60 | 60 | ASTM D2240 | ||
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | Extension rate 2 in/min; ASTM D638 | ||
| Elongation at Break | 800 % | 800 % | Extension rate 2 in/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 127 °C | 261 °F | ASTM D3417 | ||
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| Filler % | 2.5 | Carbon Black per ASTM D4218 | |||