- 熔体流动速率 [g/10min]: 0.22
- 弯曲模量 [MPa]: 0.810
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.942 g/cc | 0.942 g/cc | ISO 1183 |
| Melt Flow | 0.22 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.22 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| 17.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 17.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 22.0 MPa @Thickness 0.0400 mm | 3190 psi @Thickness 0.00157 in | ISO 527-3 |
| 23.0 MPa @Thickness 0.0200 mm | 3340 psi @Thickness 0.000787 in | ISO 527-3 | |
| Film Tensile Strength at Yield, TD | 22.0 MPa @Thickness 0.0400 mm | 3190 psi @Thickness 0.00157 in | ISO 527-3 |
| 24.0 MPa @Thickness 0.0200 mm | 3480 psi @Thickness 0.000787 in | ISO 527-3 | |
| Film Elongation at Break, MD | 450 % @Thickness 0.0200 mm | 450 % @Thickness 0.000787 in | ISO 527-3 |
| 580 % @Thickness 0.0400 mm | 580 % @Thickness 0.00157 in | ISO 527-3 | |
| Film Elongation at Break, TD | 540 % @Thickness 0.0200 mm | 540 % @Thickness 0.000787 in | ISO 527-3 |
| 660 % @Thickness 0.0400 mm | 660 % @Thickness 0.00157 in | ISO 527-3 | |
| Flexural Modulus | 0.810 GPa @Strain <=0.250 % | 117 ksi @Strain <=0.250 % | ISO 178 |
| Elmendorf Tear Strength, MD | 0.800 g/micron @Thickness 0.0200 mm | 20.3 g/mil @Thickness 0.000787 in | ISO 6383-2 |
| 1.20 g/micron @Thickness 0.0400 mm | 30.5 g/mil @Thickness 0.00157 in | ISO 6383-2 | |
| Elmendorf Tear Strength, TD | 13.3 g/micron @Thickness 0.0200 mm | 338 g/mil @Thickness 0.000787 in | ISO 6383-2 |
| 15.3 g/micron @Thickness 0.0400 mm | 389 g/mil @Thickness 0.00157 in | ISO 6383-2 | |
| Dart drop Test | 145 g @Thickness 0.0200 mm | 0.320 lb @Thickness 0.000787 in | ISO 7765-1 |
| 190 g @Thickness 0.0400 mm | 0.419 lb @Thickness 0.00157 in | ISO 7765-1 | |
| Film Tensile Strength at Break, MD | 55.0 MPa @Thickness 0.0400 mm | 7980 psi @Thickness 0.00157 in | ISO 527-3 |
| 65.0 MPa @Thickness 0.0200 mm | 9430 psi @Thickness 0.000787 in | ISO 527-3 | |
| Film Tensile Strength at Break, TD | 51.0 MPa @Thickness 0.0400 mm | 7400 psi @Thickness 0.00157 in | ISO 527-3 |
| 53.0 MPa @Thickness 0.0200 mm | 7690 psi @Thickness 0.000787 in | ISO 527-3 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 261 °F | ISO 11357 |
| Vicat Softening Point | 124 °C | 255 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 190 - 220 °C | 374 - 428 °F | Extrusion |