- 熔体流动速率 [g/10min]: 0.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.934 g/cc | 0.934 g/cc | ASTM D792 |
| Water Vapor Transmission | 10.1 g/m²/day | 0.650 g/100 in²/day | ASTM E96/66 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 30 g/10 min @Load 21.6 kg, Temperature 190 °C | 30 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882, A |
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882, A |
| Coefficient of Friction | 0.40 | 0.40 | I/I; TOTAL Method |
| Elmendorf Tear Strength MD | 55 g | 55 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 400 g | 400 g | ASTM D1922 |
| Dart drop Test | 60.0 g | 0.132 lb | ASTM D1709, A |
| Film Tensile Strength at Break, MD | 44.1 MPa | 6400 psi | ASTM D882, A |
| Film Tensile Strength at Break, TD | 42.1 MPa | 6100 psi | ASTM D882, A |
| 1% Secant Modulus, MD | 365 MPa | 53000 psi | ASTM D882, A |
| 1% Secant Modulus, TD | 386 MPa | 56000 psi | ASTM D882, A |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | TOTAL Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | ASTM D3417 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 193 - 210 °C | 380 - 410 °F | Extrusion |