- 缺口冲击强度: 1.24
- 断裂伸长率 [%]: 45.0
- 弯曲模量 [MPa]: 2.88
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.20 g/cc | 2.20 g/cc | ASTM D 792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 34.0 MPa | 4930 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 5.13 GPa | 744 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 45.0 MPa | 6530 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.88 GPa | 418 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.24 J/cm @Temperature 23.0 °C | 2.32 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 3.17 J/cm @Temperature 23.0 °C | 5.94 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 169 °C @Thickness 3.20 mm | 336 °F @Thickness 0.126 in | unannealed; ASTM D 648 |