- 吸水率 [%]: 0.007
- 弯曲强度 [MPa]: 40.0
- 弯曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 | ||
| Water Absorption | 0.0070 % | 0.0070 % | 24 hours; ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 72 | 72 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D3159 | ||
| Elongation at Break | 300 % | 300 % | ASTM D3159 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| Coefficient of Friction | 0.30 - 0.40 | 0.30 - 0.40 | ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 | ||
| Surface Resistivity per Square | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Constant | 2.6 - 2.8 @Frequency 1e+6 Hz | 2.6 - 2.8 @Frequency 1e+6 Hz | ASTM D150 | ||
| Dielectric Strength | 66.92 kV/mm @Thickness 0.250 mm | 1700 kV/in @Thickness 0.00984 in | ASTM D149 | ||
| Dissipation Factor | 0.0090 @Frequency 1e+6 Hz | 0.0090 @Frequency 1e+6 Hz | ASTM D150 | ||
| Arc Resistance | 122 sec | 122 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 267 °C | 513 °F | ASTM D3418 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Oxygen Index | 30 - 32 % | 30 - 32 % | Limiting Oxygen Index; ASTM D2863 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 302 - 323 °C | 576 - 613 °F | Cure Temperature | ||
| Descriptive Properties | |||||
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | ||||
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | ||||
| Acetic Acid Transmission, g/100sq in. | 0.41 | ||||
| Acetone Transmission, g/100sq in. | 0.95 | ||||
| Acetophenone Transmission, g/100sq in. | 0.5 | ||||
| Benzene Transmission, g/100sq in. | 0.64 | ||||
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | ||||
| Chemical/Solvent Resistance | Excellent | ||||
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | ||||
| Folding Endurance, # cycles, .18-.20 mm | 10-27 E3 | ||||
| Heat of Combustion J/g | 13700 | ASTM D240 | |||
| Hexane Transmission, g/100sq in. | 0.56 | ||||
| Piperidine Transmission, g/100sq in. | 0.04 | ||||
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | ||||
| Salt Spray Resistance on aluminum, Hours | 1000 | ||||
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | ||||
| Water Transmission, g/100sq in. | 0.4 | ||||
| Weather Resistance | 15 | Years unaffected in Florida Exposure | |||