- 熔体流动速率 [g/10min]: 9.0
- 拉伸强度 [MPa]: 5.0
- 弯曲强度 [MPa]: 34.0
- 弯曲模量 [MPa]: 0.517
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.80 - 1.85 g/cc | 1.80 - 1.85 g/cc | ASTM D792 | ||
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D3159 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 34.0 MPa | 4930 psi | ASTM D1708 | ||
| 3.00 MPa @Temperature 200 °C | 435 psi @Temperature 392 °F | ASTM D1708 | |||
| Tensile Strength, Yield | 5.00 MPa @Temperature 180 °C | 725 psi @Temperature 356 °F | ASTM D1708 | ||
| Elongation at Break | 300 % | 300 % | ASTM D1708 | ||
| 550 % @Temperature 180 °C | 550 % @Temperature 356 °F | ASTM D1708 | |||
| Flexural Modulus | 0.517 GPa | 75.0 ksi | ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 230 - 245 °C | 446 - 473 °F | ASTM D3159 | ||
| Oxygen Index | >= 40 % | >= 40 % | |||
| Descriptive Properties | |||||
| Folding Endurance, # cycles, .18-.20 mm | 180000 | ||||