- 密度 [g/cm3]: 1.7
- 吸水率 [%]: 0.005
- 拉伸强度 [MPa]: 42.1
- 断裂伸长率 [%]: 170
- 弯曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| Water Absorption | 0.0050 % | 0.0050 % | ASTM D570; 24 hrs. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 42.1 MPa | 6100 psi | ASTM D638 |
| Elongation at Break | 300 % | 300 % | ASTM D638 |
| Tensile Modulus | 0.827 GPa | 120 ksi | ASTM D638 |
| Flexural Yield Strength | 170 MPa | 24600 psi | ASTM D790 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 2.5 @Frequency 1000 Hz | 2.5 @Frequency 1000 Hz | ASTM D150 |
| Dielectric Strength | 7.87 kV/mm | 200 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 131 µm/m-°C @Temperature 20.0 °C | 73.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 266 °C | 510 °F | ASTM D4591 |
| Maximum Service Temperature, Air | 154 °C | 310 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.7 °C | 125 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 31 % | 31 % | ASTM D2863 |