- 熔体流动速率 [g/10min]: 2.4
- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.15
- 拉伸强度 [MPa]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.015 % | 0.015 % | Humidity Absorption |
| Melt Flow | 2.4 g/10 min @Load 5.00 kg, Temperature 230 °C | 2.4 g/10 min @Load 11.0 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min |
| Elongation at Break | 6.0 % | 6.0 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 2.0 % | 2.0 % | 50 mm/min |
| Tensile Modulus | 7.00 GPa | 1020 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 170 °C | 338 °F | 10°C/min |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | |
| Glass Transition Temp, Tg | -42.0 °C | -43.6 °F | 10°C/min |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||