- 吸水率 [%]: 0.04
- 拉伸强度 [MPa]: 17.9
- 弯曲强度 [MPa]: 22.8
- 弯曲模量 [MPa]: 0.338
- 热变形温度 [℃]: 48.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 - 1.80 g/cc | 1.78 - 1.80 g/cc | ASTM D792 |
| Water Absorption | 0.040 - 0.070 % | 0.040 - 0.070 % | 24 hr / 20°C; ASTM D570 |
| Ash | 0.00 - 5.0 % | 0.00 - 5.0 % | Thermal Decomposition/ in air |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 - 67 | 62 - 67 | ASTM D2240 |
| Tensile Strength, Ultimate | 22.8 - 27.6 MPa | 3300 - 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 17.9 - 24.1 MPa | 2600 - 3500 psi | ASTM D638 |
| Elongation at Break | 200 - 400 % | 200 - 400 % | ASTM D638 |
| Elongation at Yield | 10 - 20 % | 10 - 20 % | ASTM D638 |
| Tensile Modulus | 0.345 - 0.621 GPa | 50.0 - 90.0 ksi | ASTM D638 |
| Flexural Strength | 13.8 - 24.1 MPa | 2000 - 3500 psi | @ 5% strain; ASTM D790 |
| Flexural Modulus | 0.338 - 0.400 GPa | 49.0 - 58.0 ksi | ASTM D790 |
| Compressive Strength | 24.1 - 31.0 MPa | 3500 - 4500 psi | ASTM D695 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.54 | 0.54 | vs. Steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.55 | 0.55 | vs. Steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 21 - 25 | 21 - 25 | CS-17 1000g:load |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | DC, 65% RH; ASTM D257 |
| Dielectric Constant | 3.8 - 4.7 @Frequency 1e+8 Hz | 3.8 - 4.7 @Frequency 1e+8 Hz | ASTM D150 |
| 10.5 - 21.1 @Frequency 100 Hz | 10.5 - 21.1 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 43.3 - 51.2 kV/mm | 1100 - 1300 kV/in | ASTM D149 |
| Dissipation Factor | 0.050 - 0.090 @Frequency 100 Hz | 0.050 - 0.090 @Frequency 100 Hz | ASTM D150 |
| 0.21 - 0.24 @Frequency 1e+8 Hz | 0.21 - 0.24 @Frequency 1e+8 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 162 - 216 µm/m-°C @Temperature 20.0 °C | 90.0 - 120 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft²-°F | ASTM D433 |
| Deflection Temperature at 0.46 MPa (66 psi) | 48.9 - 65.6 °C | 120 - 150 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.0 - 51.7 °C | 95.0 - 125 °F | ASTM D648 |
| Glass Transition Temp, Tg | -44.0 - -40.0 °C | -47.2 - -40.0 °F | (DMA) @ 1 Hz |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt. loss / in air |
| 410 °C | 770 °F | 1% wt. loss / in nitrogen | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 42 % | 42 % | Limiting, (Optional product available with higher value of 95% O2; ASTM D2868 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.41 @Temperature 25.0 °C, Wavelength 589.3 nm | 1.41 @Temperature 77.0 °F, Wavelength 589.3 nm | Sodium D line; ASTM D542 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 130 - 134 °C | 266 - 273 °F | ASTM D3418 |