- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 1.77
- 拉伸强度 [MPa]: 52.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | |
| Melt Flow | 1.1 g/10 min @Load 5.00 kg, Temperature 230 °C | 1.1 g/10 min @Load 11.0 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 6.4 @Frequency 1e+6 Hz | 6.4 @Frequency 1e+6 Hz | |
| 9.5 @Frequency 100 Hz | 9.5 @Frequency 100 Hz | ||
| Dissipation Factor | 0.069 @Frequency 100 Hz | 0.069 @Frequency 100 Hz | |
| 0.246 @Frequency 1e+6 Hz | 0.246 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 169 °C | 336 °F | 10°C/min |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||