- 熔体流动速率 [g/10min]: 4.0
- 吸水率 [%]: 0.03
- 拉伸强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.276
- 热变形温度 [℃]: 49.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.78 - 1.80 g/cc | 1.78 - 1.80 g/cc | ASTM D792 |
| Bulk Density | 0.961 g/cc | 0.0347 lb/in³ | |
| Water Absorption | 0.030 - 0.060 % @Time 86400 sec | 0.030 - 0.060 % @Time 24.0 hour | Immersion; ASTM D570 |
| Viscosity | 500000 - 1.20e+6 cP @Shear Rate 100 1/s, Temperature 232 °C | 500000 - 1.20e+6 cP @Shear Rate 100 1/s, Temperature 450 °F | Melt Viscosity; ASTM D3835 |
| Melt Flow | 4.0 - 17.5 g/10 min @Load 3.80 kg, Temperature 232 °C | 4.0 - 17.5 g/10 min @Load 8.38 lb, Temperature 450 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 57 - 62 | 57 - 62 | ASTM D2240 |
| Tensile Strength at Break | 20.0 - 27.0 MPa | 2900 - 3920 psi | ASTM D638 |
| Tensile Strength | 4.00 MPa @Strain 20.0 %, Temperature 100 °C | 580 psi @Strain 20.0 %, Temperature 212 °F | |
| 7.00 MPa @Strain 20.0 %, Temperature 70.0 °C | 1020 psi @Strain 20.0 %, Temperature 158 °F | ||
| 11.0 MPa @Strain 20.0 %, Temperature 50.0 °C | 1600 psi @Strain 20.0 %, Temperature 122 °F | ||
| 18.0 MPa @Strain 20.0 %, Temperature 23.0 °C | 2610 psi @Strain 20.0 %, Temperature 73.4 °F | ||
| Tensile Strength, Yield | 14.0 - 21.0 MPa | 2030 - 3050 psi | ASTM D638 |
| Elongation at Break | 200 - 400 % | 200 - 400 % | ASTM D638 |
| Elongation at Yield | 15 - 25 % | 15 - 25 % | ASTM D638 |
| Tensile Modulus | 0.0900 GPa @Temperature 100 °C | 13.1 ksi @Temperature 212 °F | |
| 0.100 GPa @Temperature 70.0 °C | 14.5 ksi @Temperature 158 °F | ||
| 0.180 GPa @Temperature 50.0 °C | 26.1 ksi @Temperature 122 °F | ||
| 0.276 - 0.448 GPa @Temperature 23.0 °C | 40.0 - 65.0 ksi @Temperature 73.4 °F | ASTM D638 | |
| Flexural Strength | 14.0 - 24.0 MPa @Strain 5.00 % | 2030 - 3480 psi @Strain 5.00 % | ASTM D790 |
| Flexural Modulus | 0.276 - 0.414 GPa | 40.0 - 60.0 ksi | ASTM D790 |
| Compressive Strength | 24.0 - 31.0 MPa | 3480 - 4500 psi | ASTM D695 |
| Izod Impact, Notched | >= NB | >= NB | ASTM D256 |
| Izod Impact, Unnotched | >= NB | >= NB | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.54 | 0.54 | vs. steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.55 | 0.55 | vs. steel; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 21 - 25 | 21 - 25 | 1000 g pad; CS-17 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+14 ohm-cm @Temperature 20.0 °C | 2.00e+14 ohm-cm @Temperature 68.0 °F | 65% RH; ASTM D257 |
| Dielectric Constant | 3.8 @Frequency 1.00e+8 Hz | 3.8 @Frequency 1.00e+8 Hz | ASTM D150 |
| 12.1 @Frequency 100 Hz | 12.1 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 43.3 - 51.2 kV/mm | 1100 - 1300 kV/in | ASTM D149 |
| Dissipation Factor | 0.020 - 0.24 @Frequency 100 Hz | 0.020 - 0.24 @Frequency 100 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 97.0 µm/m-°C @Temperature -40.0 °C | 53.9 µin/in-°F @Temperature -40.0 °F | |
| 171 µm/m-°C @Temperature 0.000 °C | 95.0 µin/in-°F @Temperature 32.0 °F | ||
| 162 - 216 µm/m-°C @Temperature 22.8 °C | 90.0 - 120 µin/in-°F @Temperature 73.0 °F | ASTM D696 | |
| 313 µm/m-°C @Temperature 70.0 °C | 174 µin/in-°F @Temperature 158 °F | ||
| 370 µm/m-°C @Temperature 85.0 °C | 206 µin/in-°F @Temperature 185 °F | ||
| Specific Heat Capacity | 1.17 - 1.51 J/g-°C | 0.280 - 0.360 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.144 - 0.180 W/m-K | 1.00 - 1.25 BTU-in/hr-ft²-°F | ASTM D433 |
| Melting Point | 130 - 138 °C | 266 - 280 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 65.0 °C | 120 - 149 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.0 - 51.0 °C | 95.0 - 124 °F | ASTM D648 |
| Glass Transition Temp, Tg | -42.0 - -40.0 °C @Frequency 1.00 Hz | -43.6 - -40.0 °F @Frequency 1.00 Hz | DMA |
| Decomposition Temperature | 375 °C | 707 °F | 1% wt loss / in air; TGA |
| 410 °C | 770 °F | 1% wt loss / in nitrogen; TGA | |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 43 % | 43 % | ASTM D2868 |
| 95 % | 95 % | optional products; ASTM D2868 | |