- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.04
- 缺口冲击强度: 1.06
- 拉伸强度 [MPa]: 28.0
- 断裂伸长率 [%]: 45.0
- 弯曲强度 [MPa]: 31.0
- 弯曲模量 [MPa]: 1.138
- 脆化温度 [℃]: -62.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.77 g/cc | 0.0632 - 0.0639 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | ASTM D570 |
| Linear Mold Shrinkage | 0.025 - 0.030 cm/cm | 0.025 - 0.030 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74 - 80 | 74 - 80 | ASTM D2240 |
| Tensile Strength, Ultimate | 31.0 - 41.0 MPa | 4500 - 5950 psi | ASTM D638 |
| Tensile Strength, Yield | 28.0 - 41.0 MPa | 4060 - 5950 psi | ASTM D638 |
| Elongation at Break | 50 - 250 % | 50 - 250 % | ASTM D638 |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| Tensile Modulus | 1.03 - 1.38 GPa | 149 - 200 ksi | ASTM D638 |
| Flexural Yield Strength | 45.0 - 52.0 MPa | 6530 - 7540 psi | ASTM D790 |
| Flexural Modulus | 1.138 - 1.793 GPa | 165.1 - 260.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.06 - 2.12 J/cm | 1.99 - 3.97 ft-lb/in | |
| Izod Impact, Unnotched | 8.00 - 20.0 J/cm | 15.0 - 37.5 ft-lb/in | Low Temp; ASTM D256 |
| Coefficient of Friction, Dynamic | 0.10 - 0.25 | 0.10 - 0.25 | ASTM D1894 |
| Coefficient of Friction, Static | 0.14 - 0.20 | 0.14 - 0.20 | ASTM D1894 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.10e+15 ohm-cm | 1.10e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 6.0 @Frequency 1e+6 Hz | 6.0 @Frequency 1e+6 Hz | ASTM D150 |
| 7.2 @Frequency 60 Hz | 7.2 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 10.4 kV/mm @Thickness 3.20 mm | 264 kV/in @Thickness 0.126 in | Short-Time 500 V/sec |
| Dissipation Factor | 0.030 @Frequency 60 Hz | 0.030 @Frequency 60 Hz | ASTM D150 |
| 0.16 @Frequency 1e+6 Hz | 0.16 @Frequency 1e+6 Hz | ASTM D150 | |
| Arc Resistance | >= 50 sec | >= 50 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 - 140 µm/m-°C @Temperature 20.0 °C | 44.4 - 77.8 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.30 - 1.50 J/g-°C | 0.311 - 0.359 BTU/lb-°F | DSC |
| Thermal Conductivity | 0.190 - 0.220 W/m-K | 1.32 - 1.53 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 160 °C | 320 °F | ASTM D3418 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | No oxidative or thermal degradation after 5 years at 150°C (300°F) |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 - 90.0 °C | 176 - 194 °F | TMA |
| Brittleness Temperature | <= -62.0 °C | <= -79.6 °F | ASTM D2236 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 43 % | 43 % | ASTM D2863 |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.42 | 1.42 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 215 - 232 °C | 419 - 450 °F | Preheat |