- 密度 [g/cm3]: 2.16
- 弯曲强度 [MPa]: 33.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.16 g/cc | 0.0780 lb/in³ | Sintered moldings; ASTM D4894/D4895 |
| Apparent Bulk Density | 0.820 g/cc | 0.0296 lb/in³ | DIN 53 466 |
| Linear Mold Shrinkage | 0.035 cm/cm | 0.035 in/in | cylinder; per Dyneon method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | Sintered molding, DIN 53 505 |
| Tensile Strength, Ultimate | 33.0 MPa @Thickness 0.200 mm | 4790 psi @Thickness 0.00787 in | Sintered moldings; ASTM D4894/4895 |
| Elongation at Break | 560 % | 560 % | Sintered Molding; ASTM D4894 |
| Tensile Modulus | 0.650 GPa | 94.3 ksi | Sintered Molding, DIN 53457 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Strength | 65.0 kV/mm | 1650 kV/in | 200µm film; IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 30.0 - 100 °C | 66.7 µin/in-°F @Temperature 86.0 - 212 °F | |
| 140 µm/m-°C @Temperature 30.0 - 200 °C | 77.8 µin/in-°F @Temperature 86.0 - 392 °F | ||
| 170 µm/m-°C @Temperature 30.0 - 300 °C | 94.4 µin/in-°F @Temperature 86.0 - 572 °F | ||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52 612 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous Service Temp |
| Minimum Service Temperature, Air | -200 °C | -328 °F | Continuous Service Temp |