- 密度 [g/cm3]: 1.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 - 2.00 g/cc | 0.0686 - 0.0723 lb/in³ | molded; ASTM D792 |
| Deformation | 4.0 - 6.0 % @Pressure 13.7 MPa, Time 86400 sec | 4.0 - 6.0 % @Pressure 1990 psi, Time 24.0 hour | after 24hr relaxation; ASTM D621 |
| 12 - 13.5 % @Pressure 13.7 MPa, Time 86400 sec | 12 - 13.5 % @Pressure 1990 psi, Time 24.0 hour | ASTM D621 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 - 70 | 65 - 70 | molded; ASTM D2240 |
| Tensile Strength | 8.00 - 13.0 MPa | 1160 - 1890 psi | molded; ASTM D4745 |
| Elongation at Break | 40 - 70 % | 40 - 70 % | molded; ASTM D4745 |
| Compressive Yield Strength | 12.0 - 13.5 MPa @Strain 1.00 % | 1740 - 1960 psi @Strain 1.00 % | ASTM D695 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | |
| K (wear) Factor | 20.0 - 30.0 x 10-8 mm³/N-M | 9.93 - 14.9 x 10-10 in³-min/ft-lb-hr | at PV 100; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 - 100 µm/m-°C | 36.1 - 55.6 µin/in-°F | ASTM D696 |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Minimum Service Temperature, Air | -200 °C | -328 °F | |