- 密度 [g/cm3]: 2.21
- 缺口冲击强度: 1.3
- 拉伸强度 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.21 g/cc | 0.0798 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | Glass Fibers |
| Particle Size | 40 µm | 40 µm | Average |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 59 | 59 | ISO 868 |
| Ball Indentation Hardness | 33.0 MPa | 4790 psi | ISO 2039-1 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
| Elongation at Break | 260 % | 260 % | ISO 527 |
| Izod Impact, Notched | 1.30 J/cm | 2.44 ft-lb/in | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 65.0 µm/m-°C @Temperature 20.0 °C | 36.1 µin/in-°F @Temperature 68.0 °F | ASTM E 831 |
| Melting Point | 327 °C | 621 °F | |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 370 °C | 698 °F | Molding |
| Back Pressure | 30.0 - 45.0 MPa | 4350 - 6530 psi | Molding Pressure |