  4. Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled

Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled

Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled 物性表: Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled物性表及特性介绍,Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled注塑参数详情,如需Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.59
  • 吸水率 [%]: 1.05
  • 拉伸强度 [MPa]: 140.0
  • 弯曲模量 [MPa]: 16.4
  • 热变形温度 [℃]: 245.0
 
Physical PropertiesMetricEnglishComments
Density 1.59 g/cc
@Temperature 23.0 °C		0.0574 lb/in³
@Temperature 73.4 °F		ISO 1183
Filler Content 50 %50 %ISO 1172
Water Absorption 1.05 %
@Temperature 23.0 °C		1.05 %
@Temperature 73.4 °F		50% r.h.; ISO 62
Water Absorption at Saturation 3.5 - 4.0 %3.5 - 4.0 %ISO 62
Viscosity  8000 cP
@Frequency 10000 Hz,
Temperature 322 °C		8000 cP
@Frequency 10000 Hz,
Temperature 612 °F
 10000 cP
@Frequency 10000 Hz,
Temperature 307 °C		10000 cP
@Frequency 10000 Hz,
Temperature 585 °F
 15000 cP
@Frequency 10000 Hz,
Temperature 292 °C		15000 cP
@Frequency 10000 Hz,
Temperature 558 °F
 20000 cP
@Frequency 10000 Hz,
Temperature 277 °C		20000 cP
@Frequency 10000 Hz,
Temperature 531 °F
 30000 cP
@Frequency 1000 Hz,
Temperature 322 °C		30000 cP
@Frequency 1000 Hz,
Temperature 612 °F
 40000 cP
@Frequency 1000 Hz,
Temperature 307 °C		40000 cP
@Frequency 1000 Hz,
Temperature 585 °F
 50000 cP
@Frequency 100 Hz,
Temperature 277 °C		50000 cP
@Frequency 100 Hz,
Temperature 531 °F
 70000 cP
@Frequency 1000 Hz,
Temperature 292 °C		70000 cP
@Frequency 1000 Hz,
Temperature 558 °F
 90000 cP
@Frequency 10.0 Hz,
Temperature 277 °C		90000 cP
@Frequency 10.0 Hz,
Temperature 531 °F
 90000 cP
@Frequency 100 Hz,
Temperature 322 °C		90000 cP
@Frequency 100 Hz,
Temperature 612 °F
 100000 cP
@Frequency 1000 Hz,
Temperature 277 °C		100000 cP
@Frequency 1000 Hz,
Temperature 531 °F
 110000 cP
@Frequency 10.0 Hz,
Temperature 322 °C		110000 cP
@Frequency 10.0 Hz,
Temperature 612 °F
 120000 cP
@Frequency 100 Hz,
Temperature 307 °C		120000 cP
@Frequency 100 Hz,
Temperature 585 °F
 130000 cP
@Frequency 10.0 Hz,
Temperature 307 °C		130000 cP
@Frequency 10.0 Hz,
Temperature 585 °F
 135000 cP
@Frequency 100 Hz,
Temperature 292 °C		135000 cP
@Frequency 100 Hz,
Temperature 558 °F
 160000 cP
@Frequency 10.0 Hz,
Temperature 292 °C		160000 cP
@Frequency 10.0 Hz,
Temperature 558 °F
Linear Mold Shrinkage, Flow <= 0.0030 cm/cm<= 0.0030 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.0050 cm/cm0.0050 in/inISO 294-4
Spiral Flow 536 cm211 inAkro
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 250 MPa36300 psi5 [mm/min]; ISO 527-1/2
 125 MPa
@Temperature 140 - 150 °C,
Time 1.80e+7 sec		18100 psi
@Temperature 284 - 302 °F,
Time 5000 hour		5 [mm/min], 50% Loss of Tensile Strength; ICE 216
 125 MPa
@Temperature 110 - 130 °C,
Time 7.20e+7 sec		18100 psi
@Temperature 230 - 266 °F,
Time 20000 hour		5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Tensile Stress  25.0 MPa
@Strain 0.500 %,
Temperature 60.0 °C		3630 psi
@Strain 0.500 %,
Temperature 140 °F
 30.0 MPa
@Strain 0.500 %,
Temperature 23.0 °C		4350 psi
@Strain 0.500 %,
Temperature 73.4 °F
 80.0 MPa
@Strain 1.00 %,
Temperature 120 °C		11600 psi
@Strain 1.00 %,
Temperature 248 °F
 100 MPa
@Strain 1.00 %,
Temperature 80.0 °C		14500 psi
@Strain 1.00 %,
Temperature 176 °F
 100 MPa
@Strain 2.00 %,
Temperature 120 °C		14500 psi
@Strain 2.00 %,
Temperature 248 °F
 120 MPa
@Strain 4.00 %,
Temperature 120 °C		17400 psi
@Strain 4.00 %,
Temperature 248 °F
 125 MPa
@Strain 2.00 %,
Temperature 80.0 °C		18100 psi
@Strain 2.00 %,
Temperature 176 °F
 130 MPa
@Strain 6.00 %,
Temperature 120 °C		18900 psi
@Strain 6.00 %,
Temperature 248 °F
 135 MPa
@Strain 3.00 %,
Temperature 80.0 °C		19600 psi
@Strain 3.00 %,
Temperature 176 °F
 135 MPa
@Strain 1.00 %,
Temperature 60.0 °C		19600 psi
@Strain 1.00 %,
Temperature 140 °F
 140 MPa
@Strain 4.00 %,
Temperature 80.0 °C		20300 psi
@Strain 4.00 %,
Temperature 176 °F
 145 MPa
@Strain 8.00 %,
Temperature 120 °C		21000 psi
@Strain 8.00 %,
Temperature 248 °F
 160 MPa
@Strain 1.00 %,
Temperature 23.0 °C		23200 psi
@Strain 1.00 %,
Temperature 73.4 °F
 180 MPa
@Strain 2.00 %,
Temperature 60.0 °C		26100 psi
@Strain 2.00 %,
Temperature 140 °F
 195 MPa
@Strain 3.00 %,
Temperature 60.0 °C		28300 psi
@Strain 3.00 %,
Temperature 140 °F
 235 MPa
@Strain 2.00 %,
Temperature 23.0 °C		34100 psi
@Strain 2.00 %,
Temperature 73.4 °F
Tensile Strength, Yield  140 MPa
@Temperature 80.0 °C		20300 psi
@Temperature 176 °F
 255 MPa
@Temperature 23.0 °C		37000 psi
@Temperature 73.4 °F
 265 MPa
@Temperature -20.0 °C		38400 psi
@Temperature -4.00 °F
Elongation at Break 3.0 %3.0 %5 [mm/min]; ISO 527-1/2
Creep Strength  60.0 MPa
@Time 360 sec,
Strain 0.400 %		8700 psi
@Time 0.100 hour,
Strain 0.400 %
 60.0 MPa
@Strain 0.500 %,
Time 3600 sec		8700 psi
@Strain 0.500 %,
Time 1.00 hour
 60.0 MPa
@Strain 0.600 %,
Time 36000 sec		8700 psi
@Strain 0.600 %,
Time 10.0 hour
 60.0 MPa
@Strain 0.700 %,
Time 360000 sec		8700 psi
@Strain 0.700 %,
Time 100 hour
 90.0 MPa
@Strain 0.600 %,
Time 36000 sec		13100 psi
@Strain 0.600 %,
Time 10.0 hour
 90.0 MPa
@Strain 0.650 %,
Time 360000 sec		13100 psi
@Strain 0.650 %,
Time 100 hour
 90.0 MPa
@Time 360 sec,
Strain 0.500 %		13100 psi
@Time 0.100 hour,
Strain 0.500 %
 90.0 MPa
@Strain 0.550 %,
Time 3600 sec		13100 psi
@Strain 0.550 %,
Time 1.00 hour
 100 MPa
@Strain 0.650 %,
Time 3600 sec		14500 psi
@Strain 0.650 %,
Time 1.00 hour
 100 MPa
@Strain 0.700 %,
Time 36000 sec		14500 psi
@Strain 0.700 %,
Time 10.0 hour
 100 MPa
@Strain 0.800 %,
Time 360000 sec		14500 psi
@Strain 0.800 %,
Time 100 hour
 100 MPa
@Strain 0.880 %,
Time 3.60e+6 sec		14500 psi
@Strain 0.880 %,
Time 1000 hour
Tensile Modulus 17.5 GPa2540 ksi1[mm/min]; ISO 527-1/2
Flexural Strength 380 MPa55100 psi2 [mm/min]; ISO 178
Flexural Modulus 16.4 GPa2380 ksi2 [mm/min]; ISO 178
Charpy Impact Unnotched  9.50 J/cm²
@Temperature -30.0 °C		45.2 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 10.5 J/cm²
@Temperature 23.0 °C		50.0 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  1.50 J/cm²
@Temperature -30.0 °C		7.14 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.70 J/cm²
@Temperature 23.0 °C		8.09 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Dielectric Constant 4.424.421 MHz; IEC 60250
Comparative Tracking Index 600 V600 VTest Solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 15.0 µm/m-°C
@Temperature 23.0 - 80.0 °C		8.33 µin/in-°F
@Temperature 73.4 - 176 °F		ISO 11359-1/2
CTE, linear, Transverse to Flow 65.0 µm/m-°C
@Temperature 23.0 - 80.0 °C		36.1 µin/in-°F
@Temperature 73.4 - 176 °F		ISO 11359-1/2
Melting Point 255 °C491 °FISO 11357-1, DSC,10 [K/min]
Deflection Temperature at 0.46 MPa (66 psi) 245 °C473 °FHDT/B; ISO 75-1/2
Deflection Temperature at 1.8 MPa (264 psi) 225 °C437 °FHDT/A; ISO 75-1/2
Flammability, UL94 HB
@Thickness 0.800 mm		HB
@Thickness 0.0315 in
 
Processing PropertiesMetricEnglishComments
Feed Temperature 80.0 °C176 °F
Nozzle Temperature 290 - 310 °C554 - 590 °F
Zone 1 275 - 305 °C527 - 581 °F
Zone 2 275 - 305 °C527 - 581 °F
Zone 3 275 - 305 °C527 - 581 °F
Zone 4 275 - 305 °C527 - 581 °F
Melt Temperature 290 - 310 °C554 - 590 °F
Mold Temperature 80.0 - 120 °C176 - 248 °F
Drying Temperature 80.0 °C176 °F
Dry Time 4 - 8 hour4 - 8 hour
Injection Pressure 100 MPa14500 psi
Hold Pressure 30.0 - 80.0 MPa4350 - 11600 psi
Back Pressure 0.500 - 1.50 MPa72.5 - 218 psi
 
Descriptive Properties
Rate acc. FMVSS 302 (<100/min)Passed
Rate acc. FMVSS 302,(<100/min)FMVSS 302, >1 [mm] Thickness

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-44246.html

免责声明: 本文 Akro-Plastic Akroloy® PA GF 50 (2706) PA 6.6 & PA6I/6T Dry, 50% Glass Filled 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络