- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 0.8
- 弯曲模量 [MPa]: 20.0
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.72 g/cc @Temperature 23.0 °C | 0.0621 lb/in³ @Temperature 73.4 °F | ISO 1183 | ||
| Filler Content | 60 % | 60 % | ISO 1172 | ||
| Water Absorption | 0.80 % @Temperature 23.0 °C | 0.80 % @Temperature 73.4 °F | 50% r.h.; ISO 62 | ||
| Water Absorption at Saturation | 3.0 - 3.5 % | 3.0 - 3.5 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | <= 0.0030 cm/cm | <= 0.0030 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 | ||
| Spiral Flow | 468 cm | 184 in | Akro | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 275 MPa | 39900 psi | 5 [mm/min]; ISO 527-1/2 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5 [mm/min]; ISO 527-1/2 | ||
| Tensile Modulus | 21.0 GPa | 3050 ksi | 1[mm/min]; ISO 527-1/2 | ||
| Flexural Strength | 405 MPa | 58700 psi | 2 [mm/min]; ISO 178 | ||
| Flexural Modulus | 20.0 GPa | 2900 ksi | 2 [mm/min]; ISO 178 | ||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.60 J/cm² @Temperature 23.0 °C | 7.61 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 9.10e+13 ohm-cm | 9.10e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.50e+17 ohm | 1.50e+17 ohm | IEC 60093 | ||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 8.33 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/2 | ||
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 30.6 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/2 | ||
| Melting Point | 255 °C | 491 °F | ISO 11357-1, DSC,10 [K/min] | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | HDT/B; ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | HDT/A; ISO 75-1/2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 80.0 °C | 176 °F | |||
| Nozzle Temperature | 290 - 310 °C | 554 - 590 °F | |||
| Zone 1 | 275 - 305 °C | 527 - 581 °F | |||
| Zone 2 | 275 - 305 °C | 527 - 581 °F | |||
| Zone 3 | 275 - 305 °C | 527 - 581 °F | |||
| Zone 4 | 275 - 305 °C | 527 - 581 °F | |||
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 - 8 hour | 4 - 8 hour | |||
| Injection Pressure | 100 MPa | 14500 psi | |||
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | |||
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi | |||
| Descriptive Properties | |||||
| Rate acc. FMVSS 302 (<100/min) | Passed | ||||
| Rate acc. FMVSS 302,(<100/min) | FMVSS 302, >1 [mm] Thickness | ||||