- 密度 [g/cm3]: 1.24
- 吸水率 [%]: 8.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.0 % | 8.0 % | ISO 62 | ||
| Moisture Absorption | 3.00 % | 3.00 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 75.0 MPa | 10900 psi | conditioned; ISO 2039-1 | ||
| 150 MPa | 21800 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | conditioned; ISO 527-1/-2 | ||
| 105 MPa | 15200 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 | ||
| 7.0 % | 7.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 3.30 GPa | 479 ksi | conditioned; ISO 527-1/-2 | ||
| 6.30 GPa | 914 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | dry; ISO 179/1eU | ||
| 6.50 J/cm² | 30.9 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 5.00 J/cm² @Temperature 30.0 °C | 23.8 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 5.00 J/cm² @Temperature 30.0 °C | 23.8 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.00 J/cm² | 4.76 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.500 J/cm² @Temperature 30.0 °C | 2.38 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.500 J/cm² @Temperature 30.0 °C | 2.38 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | conditioned; IEC 60093 | ||
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | conditioned; IEC 60243-1 | ||
| 40.0 kV/mm | 1020 kV/in | dry; IEC 60243-1 | |||
| Comparative Tracking Index | 550 V | 550 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 65.0 °C | 149 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Air intake sytems | ||||
| Form | Granules | ||||
| Processing | Extrusion - blow molding | ||||
| Other Extrusion | |||||
| Product Attributes | Nanocomposite | ||||
| Special Characteristics | Improved heat resistance | ||||