- 密度 [g/cm3]: 1.36
- 缺口冲击强度: 5.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 80 | 80 | Conditioned; ISO 868 |
| 84 | 84 | ISO 868 | |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | Conditioned; ISO R 527 |
| 105 MPa | 15200 psi | ISO R 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | ISO R 527 |
| 9.0 % | 9.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 3.50 GPa | 508 ksi | Conditioned; ISO 178 |
| 7.50 GPa | 1090 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO 180/1A |
| 7.00 kJ/m² | 3.33 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179/IeU |
| 6.00 J/cm² | 28.6 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/IeA |
| 0.700 J/cm² | 3.33 ft-lb/in² | Conditioned; ISO 179/IeA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Comparative Tracking Index | 600 V | 600 V | CEI 60112/Solution A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM E831 |
| Melting Point | 243 °C | 469 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-2/AF |