- 密度 [g/cm3]: 1.72
- 吸水率 [%]: 5.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 % | 5.0 % | ISO 62 | ||
| Moisture Absorption | 1.20 % | 1.20 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 198 MPa | 28700 psi | conditioned; ISO 2039-1 | ||
| 317 MPa | 46000 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 159 MPa | 23100 psi | conditioned; ISO 527-1/-2 | ||
| 242 MPa | 35100 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 2.2 % | 2.2 % | dry; ISO 527-1/-2 | ||
| 3.6 % | 3.6 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 13.0 GPa | 1890 ksi | conditioned; ISO 527-1/-2 | ||
| 20.0 GPa | 2900 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 8.60 J/cm² | 40.9 ft-lb/in² | dry; ISO 179/1eU | ||
| 9.10 J/cm² | 43.3 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 7.60 J/cm² @Temperature 30.0 °C | 36.2 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 8.60 J/cm² @Temperature 30.0 °C | 40.9 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | dry; ISO 179/1eA | ||
| 1.80 J/cm² | 8.57 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 1.10 J/cm² @Temperature 30.0 °C | 5.23 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| 1.15 J/cm² @Temperature 30.0 °C | 5.47 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C | 7.22 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C | 48.3 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 265 °C | 509 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 130 - 150 °C | 266 - 302 °F | long term; EMS | ||
| 230 °C | 446 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Automotive | Air intake sytems | ||||
| Automotive electr. and electronics, lighting | |||||
| Cooling and climate control | |||||
| Hydraulic systems | |||||
| Electricals & Electronics | Lighting | ||||
| Form | Granules | ||||
| Industry & Consumer goods | Heating systems | ||||
| Hydraulics & Pneumatics | |||||
| Mechanical Engineering | |||||
| Sports & Leisure | |||||
| Processing | Injection Molding | ||||
| Special Characteristics | Improved heat resistance | ||||