- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 3.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Water Absorption | 3.5 % | 3.5 % | ISO 62 | ||
| Moisture Absorption | 1.30 % | 1.30 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 230 MPa | 33400 psi | conditioned; ISO 2039-1 | ||
| 240 MPa | 34800 psi | dry; ISO 2039-1 | |||
| Tensile Strength at Break | 130 MPa | 18900 psi | conditioned; ISO 527-1/-2 | ||
| 140 MPa | 20300 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 2.0 % | 2.0 % | dry; ISO 527-1/-2 | ||
| 2.0 % | 2.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 10.5 GPa | 1520 ksi | conditioned; ISO 527-1/-2 | ||
| 10.5 GPa | 1520 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | dry; ISO 179/1eU | ||
| 4.00 J/cm² | 19.0 ft-lb/in² | conditioned; ISO 179/1eU | |||
| 3.50 J/cm² @Temperature 30.0 °C | 16.7 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 3.50 J/cm² @Temperature 30.0 °C | 16.7 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.700 J/cm² | 3.33 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.600 J/cm² @Temperature 30.0 °C | 2.86 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.600 J/cm² @Temperature 30.0 °C | 2.86 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | dry; IEC 60093 | ||
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | conditioned; IEC 60093 | |||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | dry; IEC 60243-1 | ||
| 34.0 kV/mm | 864 kV/in | conditioned; IEC 60243-1 | |||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C | 25.0 µin/in-°F | ISO 11359-1/-2 | ||
| Melting Point | 310 °C | 590 °F | 10°C/min; ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 150 °C | 302 °F | long term; EMS | ||
| 240 °C | 464 °F | short term; EMS | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 8.0 MPa | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 | V-0 | IEC 60695-11-10 | ||
| 5VA | 5VA | IEC 60695-11-20 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| Oxygen Index | 35 % | 35 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Interior | |||||
| Electricals & Electronics | Connectors | ||||
| Electrical appliances | |||||
| Electrical equipment | |||||
| Energy distribution | |||||
| Lighting | |||||
| Mobile phones and other portable devices | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Hydraulics & Pneumatics | ||||
| Mechanical Engineering | |||||
| Power transmission | |||||
| Tools & Accessories | |||||
| Processing | Injection Molding | ||||
| Product Attributes | Co Polyamide | ||||
| Improved alcohol resistance | |||||
| Improved flowability and demoulding | |||||
| Partially aromatic Polyamide | |||||
| Special Characteristics | Flame retardant | ||||
| Improved heat resistance | |||||