- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 1.1
- 拉伸强度 [MPa]: 40.0
- 断裂伸长率 [%]: 70.0
- 弯曲强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183-A |
| Water Absorption | 1.1 % | 1.1 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | 100 % | 100 % | ISO 527 |
| Elongation at Yield | 13 % | 13 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact Resistance | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB | NB | ISO 179/EU-1993 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1EA-1993 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243-1 |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz | 0.060 @Frequency 1e+6 Hz | IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 242 °C | 468 °F | ISO 3146-C |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Middle Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |