- 密度 [g/cm3]: 1.15
- 缺口冲击强度: 3.5
- 弯曲模量 [MPa]: 3.07
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 | ||
| Elongation at Break | 32 % | 32 % | ISO 527 | ||
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 | ||
| Flexural Modulus | 3.07 GPa | 445 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180 | ||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 0.340 J/cm² | 1.62 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | CEI 93 | ||
| Dielectric Constant | 2.9 | 2.9 | CEI 250 | ||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | CEI 93 | ||
| Dissipation Factor | 0.030 | 0.030 | CEI 250 | ||
| Comparative Tracking Index | 600 V | 600 V | CEI 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ISO 75 | ||
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |||
| Glow Wire Test | 960 °C | 1760 °F | CEI 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Descriptive Properties | |||||
| Compression Zone | 270-285°C | ||||
| Mixing Zone | 270-285°C | ||||