| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Relative Viscosity | 3.99 - 4.17 cP | 3.99 - 4.17 cP | 96% H2SO4 | ||
| 4.3 - 4.5 cP | 4.3 - 4.5 cP | 98% H2SO4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 510 % | 510 % | |||
| Film Elongation at Break, TD | 560 % | 560 % | |||
| Secant Modulus, MD | 0.190 GPa | 27.6 ksi | |||
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | |||
| Coefficient of Friction, Dynamic | 0.51 | 0.51 | |||
| Coefficient of Friction, Static | 0.94 | 0.94 | |||
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | |||
| Film Tensile Strength at Break, TD | 43.0 MPa | 6240 psi | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 191 - 201 °C | 376 - 394 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11.7 % | 11.7 % | |||
| Gloss | 112 % | 112 % | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 190 - 210 °C | 374 - 410 °F | C1 | ||
| 220 - 230 °C | 428 - 446 °F | C2 | |||
| 230 - 240 °C | 446 - 464 °F | C3 | |||
| 230 - 240 °C | 446 - 464 °F | C4 | |||
| 240 - 250 °C | 464 - 482 °F | AD | |||
| 240 - 250 °C | 464 - 482 °F | CF | |||
| 240 - 250 °C | 464 - 482 °F | D1- D4 | |||
| Descriptive Properties | |||||
| Degree of Curling | 8 Mm | ||||