- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.76
- 拉伸强度 [MPa]: 228.0
- 断裂伸长率 [%]: 331
- 弯曲模量 [MPa]: 14.5
- 硬度: 121.0
- 热变形温度 [℃]: 257.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % @Time 86400 sec | 0.40 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm | 0.0040 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 228 MPa | 33000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 331 MPa | 48000 psi | ASTM D790 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm @Thickness 3.17 mm | 3.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.5 kV/mm | 470 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 14.4 µm/m-°C | 8.00 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |