- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 1.2
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Water Absorption | 1.2 % | 1.2 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D551 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ISO 527-1 |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527-1 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-1 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Charpy Impact Unnotched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | ASTM E1461 |
| Thermal Conductivity | 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | ASTM E1461 |
| Flammability, UL94 | V-0 @Thickness 1.00 mm | V-0 @Thickness 0.0394 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 290 - 310 °C | 554 - 590 °F | |
| Middle Barrel Temperature | 300 - 315 °C | 572 - 599 °F | |
| Front Barrel Temperature | 305 - 320 °C | 581 - 608 °F | |
| Nozzle Temperature | 310 - 330 °C | 590 - 626 °F | |
| Melt Temperature | 310 - 316 °C | 590 - 601 °F | |
| Mold Temperature | 80.0 - 150 °C | 176 - 302 °F | |
| Drying Temperature | 104 °C | 219 °F | |
| Dry Time | 12 hour | 12 hour | |
| Moisture Content | 0.050 % | 0.050 % | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 70.0 - 105 MPa | 10200 - 15200 psi | |
| Hold Pressure | 35.0 - 70.0 MPa | 5080 - 10200 psi | |
| Back Pressure | 0.000 - 0.700 MPa | 0.000 - 102 psi | |
| Screw Speed | 50 - 150 rpm | 50 - 150 rpm | |