- 密度 [g/cm3]: 1.25
- 拉伸强度 [MPa]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 3.2 % | 3.2 % | 50% RH / 23°C; Similar to ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ISO 527-1/-2 |
| Elongation at Yield | 25 % | 25 % | Nominal Strain at Yield; ISO 527-1/-2 |
| Tensile Modulus | 2.90 GPa | 421 ksi | ISO 527-1/-2 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eU |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |