- 密度 [g/cm3]: 1.41
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | (DAM); ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | DAM; ISO 294-4 | ||
| 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-1/-2 | ||
| Elongation at Break | 6.0 % | 6.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C | 6.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.70 J/cm² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1000 hours | 4500 MPa | 653000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | PLC 2; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 295 °C | 563 °F | 10°C/min (DAM); ISO 11357-1/-3 | ||
| UL RTI, Electrical | 140 °C @Thickness 0.900 mm | 284 °F @Thickness 0.0354 in | UL746B | ||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical with Impact | 120 °C @Thickness 0.900 mm | 248 °F @Thickness 0.0354 in | UL746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 0.900 mm | 248 °F @Thickness 0.0354 in | UL746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | |||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||