- 密度 [g/cm3]: 1.51
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | Parallel; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Normal; ISO 194-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature -30.0 °C | 35.7 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 8.50 J/cm² @Temperature 23.0 °C | 40.5 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 |