- 吸水率 [%]: 0.7
- 缺口冲击强度: 0.834
- 拉伸强度 [MPa]: 123.0
- 断裂伸长率 [%]: 186
- 弯曲模量 [MPa]: 7.65
- 硬度: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Water Absorption | 0.70 % @Temperature 23.0 °C, Time 86400 sec | 0.70 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D570 |
| Maximum Moisture Content | 0.090 | 0.090 | Injection Molding |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength, Yield | 123 MPa @Thickness 3.20 mm | 17800 psi @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.20 mm | 3.0 % @Thickness 0.126 in | 5mm/min; ASTM D638 |
| Flexural Yield Strength | 186 MPa @Thickness 3.20 mm | 27000 psi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Flexural Modulus | 7.65 GPa @Thickness 3.20 mm | 1110 ksi @Thickness 0.126 in | 1.3mm/min; ASTM D790 |
| Izod Impact, Notched | 0.834 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.56 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz | 3.0 @Frequency 1.00e+6 Hz | ASTM D150 |
| Dielectric Strength | 22.0 kV/mm @Thickness 1.00 mm | 559 kV/in @Thickness 0.0394 in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 6.40 mm | 473 °F @Thickness 0.252 in | Unannealed; ASTM D648 |
| UL RTI, Electrical | 65.0 °C @Thickness >=0.800 mm | 149 °F @Thickness >=0.0315 in | |
| 65.0 °C @Thickness >=1.50 mm | 149 °F @Thickness >=0.0591 in | ||
| 65.0 °C @Thickness >=3.00 mm | 149 °F @Thickness >=0.118 in | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness >=0.800 mm | 149 °F @Thickness >=0.0315 in | |
| 65.0 °C @Thickness >=1.50 mm | 149 °F @Thickness >=0.0591 in | ||
| 65.0 °C @Thickness >=3.00 mm | 149 °F @Thickness >=0.118 in | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness >=0.800 mm | 149 °F @Thickness >=0.0315 in | |
| 65.0 °C @Thickness >=1.50 mm | 149 °F @Thickness >=0.0591 in | ||
| 65.0 °C @Thickness >=3.00 mm | 149 °F @Thickness >=0.118 in | ||
| Flammability, UL94 | V-0 @Thickness >=0.800 mm | V-0 @Thickness >=0.0315 in | |
| V-0 @Thickness >=1.50 mm | V-0 @Thickness >=0.0591 in | ||
| V-0 @Thickness >=3.00 mm | V-0 @Thickness >=0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 265 - 275 °C | 509 - 527 °F | Injection Molding |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Front Barrel Temperature | 270 - 285 °C | 518 - 545 °F | Injection Molding |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |