- 密度 [g/cm3]: 1.18
- 吸水率 [%]: 9.5
- 拉伸强度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183-1 | ||
| Moisture Absorption at Equilibrium | 2.8 % @Temperature 23.0 °C | 2.8 % @Temperature 73.4 °F | 50% RH | ||
| Water Absorption at Saturation | 9.5 % @Temperature 23.0 °C | 9.5 % @Temperature 73.4 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 92 | 92 | ISO 2039-2 | ||
| Hardness, Shore D | 80 | 80 | DIN 53505 | ||
| Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50% RH; ISO 527-1/-2 | ||
| 105 MPa | 15200 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | 25 % | 25 % | dry; ISO 527-1/-2 | ||
| >= 100 % | >= 100 % | 50% RH; ISO 527-1/-2 | |||
| Creep Strength | 7.50 MPa | 1090 psi | stress leading to 1% elongation; 50% RH; ISO 899-1 | ||
| 22.0 MPa | 3190 psi | stress leading to 1% elongation; dry; ISO 899-1 | |||
| Modulus of Elasticity | 1.35 GPa | 196 ksi | 50% RH | ||
| 3.40 GPa | 493 ksi | dry | |||
| Compressive Yield Strength | 23.0 MPa @Strain 1.00 % | 3340 psi @Strain 1.00 % | dry; ISO 604 | ||
| 45.0 MPa @Strain 2.00 % | 6530 psi @Strain 2.00 % | dry; ISO 604 | |||
| 94.0 MPa @Strain 5.00 % | 13600 psi @Strain 5.00 % | dry; ISO 604 | |||
| Charpy Impact Unnotched | NB | NB | ISO 179-1/1eU | ||
| NB | NB | ISO 179 | |||
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179-1/1eA | ||
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | >= 1.00e+12 ohm-cm | >= 1.00e+12 ohm-cm | 50% RH; IEC 60093 | ||
| >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | dry; IEC 60093 | |||
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | 50% RH; IEC 60093 | ||
| >= 1.00e+13 ohm | >= 1.00e+13 ohm | dry; IEC 60093 | |||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | dry; IEC 60250 | ||
| 3.5 @Frequency 100 Hz | 3.5 @Frequency 100 Hz | dry; IEC 60250 | |||
| 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | 50% RH; IEC 60250 | |||
| 7.4 @Frequency 100 Hz | 7.4 @Frequency 100 Hz | 50% RH; IEC 60250 | |||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | 50% RH; IEC 60243-1 | ||
| 25.0 kV/mm | 635 kV/in | dry; IEC 60243-1 | |||
| Dielectric Loss Index | 0.0090 @Frequency 100 Hz | 0.0090 @Frequency 100 Hz | dry; IEC 60250 | ||
| 0.019 @Frequency 1.00e+6 Hz | 0.019 @Frequency 1.00e+6 Hz | dry; IEC 60250 | |||
| 0.060 @Frequency 1.00e+6 Hz | 0.060 @Frequency 1.00e+6 Hz | 50% RH; IEC 60250 | |||
| 0.13 @Frequency 100 Hz | 0.13 @Frequency 100 Hz | 50% RH; IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C | 44.4 µin/in-°F @Temperature 73.4 - 140 °F | |||
| 90.0 µm/m-°C @Temperature 23.0 - 100 °C | 50.0 µin/in-°F @Temperature 73.4 - 212 °F | ||||
| Melting Point | 290 °C | 554 °F | ISO 11357-1 | ||
| Maximum Service Temperature, Air | 130 °C @Time 7.20e+7 sec | 266 °F @Time 20000 hour | |||
| 150 °C @Time 1.80e+7 sec | 302 °F @Time 5000 hour | ||||
| 200 °C @Time <=86400 sec | 392 °F @Time <=24.0 hour | ||||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | ISO 11357-1 | ||
| Flammability, UL94 | HB | HB | |||
| Compliance Properties | Metric | English | Comments | ||
| FDA | Yes | Yes | |||
| Descriptive Properties | |||||
| Color | Auburn | ||||