- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 0.35
- 缺口冲击强度: 0.267
- 拉伸强度 [MPa]: 71.7
- 断裂伸长率 [%]: 90.0
- 弯曲强度 [MPa]: 3.6
- 弯曲模量 [MPa]: 3.10
- 硬度: 112.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 - 1.73 g/cc | 0.0444 - 0.0625 lb/in³ | Average value: 1.45 g/cc Grade Count:108 |
| Filler Content | 10.0 - 45.0 % | 10.0 - 45.0 % | Average value: 29.2 % Grade Count:28 |
| Water Absorption | 0.350 - 5.40 % | 0.350 - 5.40 % | Average value: 1.35 % Grade Count:52 |
| Moisture Absorption at Equilibrium | 1.10 - 2.00 % | 1.10 - 2.00 % | Average value: 1.50 % Grade Count:8 |
| Viscosity | 30.0 - 120 cP @Temperature 280 - 300 °C | 30.0 - 120 cP @Temperature 536 - 572 °F | Average value: 70.7 cP Grade Count:1 |
| 30.0 - 120 cP @Shear Rate 100 - 1000 1/s | 30.0 - 120 cP @Shear Rate 100 - 1000 1/s | Average value: 70.7 cP Grade Count:1 | |
| Viscosity Measurement | 0.800 - 136 | 0.800 - 136 | Average value: 68.5 Grade Count:4 |
| Linear Mold Shrinkage | 0.00150 - 0.0335 cm/cm | 0.00150 - 0.0335 in/in | Average value: 0.00614 cm/cm Grade Count:100 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00700 cm/cm | 0.00500 - 0.00700 in/in | Average value: 0.00586 cm/cm Grade Count:7 |
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.0140 cm/cm | 0.00600 - 0.0140 in/in | Average value: 0.00938 cm/cm Grade Count:32 |
| Melt Flow | 2.00 - 44.4 g/10 min | 2.00 - 44.4 g/10 min | Average value: 19.4 g/10 min Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 74.0 - 98.0 | 74.0 - 98.0 | Average value: 93.8 Grade Count:8 |
| Hardness, Rockwell R | 112 - 122 | 112 - 122 | Average value: 120 Grade Count:36 |
| Tensile Strength, Ultimate | 3.60 - 165 MPa | 522 - 23900 psi | Average value: 78.4 MPa Grade Count:74 |
| 44.0 - 145 MPa @Temperature -40.0 - 121 °C | 6380 - 21000 psi @Temperature -40.0 - 250 °F | Average value: 51.1 MPa Grade Count:1 | |
| 1.60 - 202.6 MPa @Temperature -40.0 - 150 °C | 232 - 29380 psi @Temperature -40.0 - 302 °F | Average value: 51.1 MPa Grade Count:5 | |
| 1.60 - 202.6 MPa @Strain 0.100 - 15.0 % | 232 - 29380 psi @Strain 0.100 - 15.0 % | Average value: 51.1 MPa Grade Count:5 | |
| Tensile Strength, Yield | 71.7 - 162 MPa | 10400 - 23500 psi | Average value: 119 MPa Grade Count:37 |
| Elongation at Break | 1.00 - 12.0 % | 1.00 - 12.0 % | Average value: 3.54 % Grade Count:103 |
| 3.00 - 18.0 % @Temperature -40.0 - 121 °C | 3.00 - 18.0 % @Temperature -40.0 - 250 °F | Average value: 11.8 % Grade Count:1 | |
| Elongation at Yield | 2.30 - 6.00 % | 2.30 - 6.00 % | Average value: 4.36 % Grade Count:4 |
| Modulus of Elasticity | 3.70 - 13.1 GPa | 537 - 1900 ksi | Average value: 8.17 GPa Grade Count:41 |
| Flexural Yield Strength | 90.0 - 248 MPa | 13100 - 36000 psi | Average value: 176 MPa Grade Count:86 |
| Flexural Modulus | 3.10 - 12.5 GPa | 450 - 1810 ksi | Average value: 7.44 GPa Grade Count:102 |
| 1.38 - 6.895 GPa @Temperature -40.0 - 121 °C | 200 - 1000 ksi @Temperature -40.0 - 250 °F | Average value: 3.33 GPa Grade Count:1 | |
| Compressive Yield Strength | 138 - 255 MPa | 20000 - 37000 psi | Average value: 179 MPa Grade Count:6 |
| Poissons Ratio | 0.260 - 0.470 @Temperature -40.0 - 121 °C | 0.260 - 0.470 @Temperature -40.0 - 250 °F | Average value: 0.383 Grade Count:1 |
| Shear Modulus | 0.249 - 2.569 GPa @Temperature -50.0 - 250 °C | 36.1 - 372.6 ksi @Temperature -58.0 - 482 °F | Average value: 1.27 GPa Grade Count:1 |
| Izod Impact, Notched | 0.267 - 1.33 J/cm | 0.500 - 2.50 ft-lb/in | Average value: 0.536 J/cm Grade Count:75 |
| 0.320 - 0.380 J/cm @Temperature -40.0 - -40.0 °C | 0.599 - 0.712 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 0.350 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 3.20 - 9.08 J/cm | 6.00 - 17.0 ft-lb/in | Average value: 5.51 J/cm Grade Count:31 |
| Izod Impact, Notched (ISO) | 2.60 - 16.0 kJ/m² | 1.24 - 7.61 ft-lb/in² | Average value: 5.29 kJ/m² Grade Count:28 |
| 3.40 - 7.50 kJ/m² @Temperature -40.0 - -30.0 °C | 1.62 - 3.57 ft-lb/in² @Temperature -40.0 - -22.0 °F | Average value: 4.32 kJ/m² Grade Count:6 | |
| Izod Impact, Unnotched (ISO) | 40.0 - 50.0 kJ/m² @Temperature -30.0 - -30.0 °C | 19.0 - 23.8 ft-lb/in² @Temperature -22.0 - -22.0 °F | Average value: 45.0 kJ/m² Grade Count:1 |
| Charpy Impact Unnotched | 2.50 - 9.00 J/cm² | 11.9 - 42.8 ft-lb/in² | Average value: 4.96 J/cm² Grade Count:22 |
| 3.50 - 5.00 J/cm² @Temperature -30.0 - -20.0 °C | 16.7 - 23.8 ft-lb/in² @Temperature -22.0 - -4.00 °F | Average value: 4.09 J/cm² Grade Count:9 | |
| Charpy Impact, Notched | 0.300 - 1.60 J/cm² | 1.43 - 7.61 ft-lb/in² | Average value: 0.566 J/cm² Grade Count:26 |
| 0.250 - 0.700 J/cm² @Temperature -40.0 - -20.0 °C | 1.19 - 3.33 ft-lb/in² @Temperature -40.0 - -4.00 °F | Average value: 0.390 J/cm² Grade Count:13 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+9 - 1.00e+17 ohm-cm | 1.00e+9 - 1.00e+17 ohm-cm | Average value: 2.65e+15 ohm-cm Grade Count:43 |
| Surface Resistance | 1.00e+10 - 3.00e+14 ohm | 1.00e+10 - 3.00e+14 ohm | Average value: 5.52e+13 ohm Grade Count:10 |
| Dielectric Constant | 3.00 - 13.9 | 3.00 - 13.9 | Average value: 4.81 Grade Count:14 |
| Dielectric Strength | 15.7 - 40.0 kV/mm | 399 - 1020 kV/in | Average value: 22.9 kV/mm Grade Count:33 |
| Dissipation Factor | 0.0100 - 0.540 | 0.0100 - 0.540 | Average value: 0.0666 Grade Count:8 |
| Dielectric Loss Index | 0.0150 - 0.150 | 0.0150 - 0.150 | Average value: 0.0825 Grade Count:4 |
| Arc Resistance | 125 - 130 sec | 125 - 130 sec | Average value: 128 sec Grade Count:4 |
| Comparative Tracking Index | 375 - 600 V | 375 - 600 V | Average value: 445 V Grade Count:11 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.100 - 500 µm/m-°C | 0.0556 - 278 µin/in-°F | Average value: 168 µm/m-°C Grade Count:36 |
| 500 - 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 µin/in-°F @Temperature 131 - 320 °F | Average value: 500 µm/m-°C Grade Count:2 | |
| CTE, linear, Transverse to Flow | 0.500 - 100 µm/m-°C | 0.278 - 55.6 µin/in-°F | Average value: 63.8 µm/m-°C Grade Count:7 |
| 100 - 100 µm/m-°C @Temperature 55.0 - 160 °C | 55.6 - 55.6 µin/in-°F @Temperature 131 - 320 °F | Average value: 100 µm/m-°C Grade Count:2 | |
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | Average value: 1.50 J/g-°C Grade Count:3 |
| Thermal Conductivity | 0.350 - 0.504 W/m-K | 2.43 - 3.50 BTU-in/hr-ft²-°F | Average value: 0.420 W/m-K Grade Count:5 |
| Melting Point | 220 - 275 °C | 428 - 527 °F | Average value: 258 °C Grade Count:57 |
| Maximum Service Temperature, Air | 145 - 254 °C | 293 - 489 °F | Average value: 196 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 263 °C | 410 - 505 °F | Average value: 250 °C Grade Count:57 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 - 257 °C | 255 - 495 °F | Average value: 226 °C Grade Count:102 |
| Vicat Softening Point | 230 - 250 °C | 446 - 482 °F | Average value: 242 °C Grade Count:5 |
| UL RTI, Electrical | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:3 |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:3 |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | Average value: 65.0 °C Grade Count:3 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:29 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 - 300 °C | 525 - 572 °F | Average value: 287 °C Grade Count:13 |
| Nozzle Temperature | 255 - 295 °C | 491 - 563 °F | Average value: 277 °C Grade Count:9 |
| Melt Temperature | 220 - 316 °C | 428 - 600 °F | Average value: 282 °C Grade Count:43 |
| Mold Temperature | 60.0 - 121 °C | 140 - 250 °F | Average value: 90.0 °C Grade Count:51 |
| Drying Temperature | 60.0 - 130 °C | 140 - 266 °F | Average value: 83.4 °C Grade Count:30 |
| Dry Time | 1.00 - 5.00 hour | 1.00 - 5.00 hour | Average value: 3.39 hour Grade Count:22 |
| <= 4.00 hour @Temperature 93.3 - 93.3 °C | <= 4.00 hour @Temperature 200 - 200 °F | Average value: 4.00 hour Grade Count:1 | |
| Moisture Content | 0.0500 - 0.200 % | 0.0500 - 0.200 % | Average value: 0.179 % Grade Count:20 |
| Injection Pressure | 4.96 - 138 MPa | 720 - 20000 psi | Average value: 79.2 MPa Grade Count:21 |
| Back Pressure | 0.000 - 58.8 MPa | 0.000 - 8530 psi | Average value: 8.30 MPa Grade Count:11 |
| Screw Speed | 20.0 - 120 rpm | 20.0 - 120 rpm | Average value: 66.4 rpm Grade Count:11 |