- 吸水率 [%]: 2.0
- 弯曲模量 [MPa]: 6.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 25 % | 25 % | ISO 1172 |
| Water Absorption | 2.0 - 2.2 % @Temperature 23.0 °C | 2.0 - 2.2 % @Temperature 73.4 °F | 50% r.h.; ISO 62 |
| Water Absorption at Saturation | 5.7 - 6.3 % @Time 82800 sec | 5.7 - 6.3 % @Time 23.0 hour | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 115 MPa | 16700 psi | 5 [mm/min]; ISO 527-1/2 |
| 57.5 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec | 8340 psi @Temperature 320 - 347 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| 57.5 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec | 8340 psi @Temperature 266 - 302 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ICE 216 | |
| Elongation at Break | 6.5 % | 6.5 % | 5 [mm/min]; ISO 527-1/2 |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1[mm/min]; ISO 527-1/2 |
| Flexural Strength | 200 MPa | 29000 psi | 2 [mm/min]; ISO 178 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 2 [mm/min]; ISO 178 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | ISO 11357-1/3 |