- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 5.9
- 弯曲强度 [MPa]: 205.0
- 热变形温度 [℃]: 257.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO data |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.9 % | 5.9 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM and ISO value |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 205 MPa | 29700 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min | |
| Tensile Modulus | 9.74 GPa | 1410 ksi | same value from ASTM and ISO test. |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 3.60 GPa | 522 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ISO data |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C @Temperature 20.0 °C | 12.8 µin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature 20.0 °C | 38.3 µin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 260 °C | 500 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO Data |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 290 °C | 554 °F | See Materials Notes |
| Mold Temperature | 80.0 °C | 176 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |