- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 0.32
- 弯曲强度 [MPa]: 82.0
- 弯曲模量 [MPa]: 6.00
- 硬度: 118.0
- 热变形温度 [℃]: 251.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 82.0 MPa | 11900 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 134 MPa | 19400 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm | 4.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 255 - 275 °C | 491 - 527 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 291 - 302 °C | 556 - 576 °F | Approximate middle barrel temperature range |