- 密度 [g/cm3]: 1.33
- 吸水率 [%]: 6.4
- 缺口冲击强度: 11.0
- 弯曲强度 [MPa]: 124.0
- 弯曲模量 [MPa]: 5.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 6.4 % | 6.4 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 124 MPa | 18000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 5.0 % | 5.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 6.30 GPa | 914 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 5.10 GPa | 740 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO Test | ||
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179 | ||
| 5.60 J/cm² @Temperature -30.0 °C | 26.7 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 179 | ||
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 257 °C | 495 °F | 10 K/min | ||
| 257 °C | 495 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||